Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Carousel with three slides shown at a time. Use the Previous and Next buttons to navigate three slides at a time, or the slide dot buttons at the end to jump three slides at a time. CAS 1313-97-9

Synthesis and electrochemical performance of α-Al2O3 and M-Al2O4 spinel nanocomposites in hybrid quantum dot-sensitized solar cells | Scientific Reports

R. Krishnapriya, C. Nizamudeen, … A.-HI Mourad

M. A. Alenizi, Rajeev Kumar, … M. A. Barakat

Mohamed Rabia, HSH Mohamed, … S. Taha

Naseer Iqbal, Adeel Afzal, Ahsanulhaq Qurashi

Muhammad Sohail, Hyunuk Kim & Tae Woo Kim

Aadil Ahmad Bhat, Shakeel Ahmad Khandy, … Radha Tomar

Kakaraparthi Kranthiraja, Mritunjaya Parashar, … Anupama B. Kaul

Shubhranshu Bhandari, Anurag Roy, … Senthilarasu Sundaram

Shuang Lu, Huanying Yang, … Xintong Zhang

Scientific Reports volume  12, Article number: 17009 (2022 ) Cite this article

The aim of this study is to describe the performance of the aluminum oxide nanoparticle and metal aluminate spinel nanoparticle as photo-anodes in quantum dot photovoltaic. By using a sol–gel auto combustion method, Al2O3 NPs, CoAl2O4, CuAl2O4, NiAl2O4, and ZnAl2O4 were successfully synthesized. The formation of Al2O3 NPs and MAl2O4 (M=Co, Cu, Ni, Zn) nanocomposite was confirmed by using several characteristics such as XRD, UV–Vis, FTIR, FE-SEM, and EDX spectra. The XRD shows that the CoAl2O4 has a smaller crystallite size (12.37 nm) than CuAl2O4, NiAl2O4, and ZnAl2O4. The formation of a single-phase spinel structure of the calcined samples at 1100 °C was confirmed by FTIR. Our studies showed that the pure Al2O3 NPs have a lower energy gap (1.37 eV) than synthesized MAl2O4 under UV–Vis irradiation. Due to the well separation between the light-generated electrons and the formed holes, the cell containing ZnAl2O4 nanocomposite with CdS QDs has the highest efficiency of 8.22% and the current density of 22.86 mA cm−2, while the cell based on NiAl2O4 as a photoelectrode, six cycles of CdS/ZnS QDs, and P-rGO as a counter electrode achieved the best (PCE) power conversion efficiency of 15.14% and the current density of 28.22 mA cm−2. Electrochemical impedance spectroscopy shows that ZnAl2O4 and NiAl2O4 nanocomposites have the highest life times of the photogenerated electrons (τn) of 11*10−2 and 96*10−3 ms, respectively, and the lowest diffusion rates (Keff) of 9.09 and 10.42 ms−1, respectively.

Alpha-alumina and metal aluminate spinel with the formula M-Al2O4, where M introduces a divalent metal ion, have attracted great attention for several applications due to their thermal stabilities, high chemical resistance and mechanical resistance, high quantum yields with hydrophobic qualities, high surface area, and low acidic surface1,2,3,4,5,6,7,8,9,10. They have been widely used as pigments, sensors, photocatalysts, magnetic, refractory, optical, and materials electrodes, involving lubricant additives11,12,13,14,15. It has been known that the synthesis method can influence the crystallinity, purity, surface area, morphology, and particle size of nanosynthesized materials MAl2O4, which has a respectable impact on their catalytic and optical properties16,17,18. MAl2O4 can be used with a variety of techniques including solvothermal method, co-precipitation synthesis, sol–gel method, solid-state reactions, hydrothermal method, microwave-assisted, polymeric precursor synthesis, and hydrothermal method16,17,18,19,20,21,22,23,24,25,26,27,28,29,30. Either method requires specialized accommodation and has a respectable cost, while further disadvantages include the shortage of homogeneity and low surface area of product5,6,7,8,9,10,16,17,18,31,32,33. The generation of the homogeneous high-purity nanoparticles has been demonstrated by the sol–gel auto combustion technique with swift heating and short reaction time11,12,34. The sol–gel auto combustion synthesis method combines chemical sol–gel and combustion processes, representing a swift, attainable technique with low energy costs, and is perfect for the synthesis of materials based on metal oxides. Several organic compounds can be utilized as the fuel, but these have been imitatively fixed to citric acid, urea, glycine, and tartaric acid7,12. Graphene is an intriguing material with a novel two-dimensional skeleton composed of a single monomolecular layer of sp2-hybridized carbon atoms1,4. Graphene has excellent properties in many areas of technology and science due to its unique properties5,6, including superior electronic6,7,8, mechanical, and thermodynamic properties9,10. Graphene has a broad domain of applications such as field-effect transistors (FET), transparent conductive films, energy storage devices, water purification, and sensors due to its elegant physical and chemical properties16,17,18,31,32. P-rGO is a carbon material that shows optical, chemical, and electrical characteristics similar to those of graphene because it is based on its framework35. In 1958, Hummers and Offman have well-educated a method for the synthesis of P-rGO36,37,38,39,40,41. This method uses H2SO4 to peel graphite with NaNO3 and KMnO4 as the oxidizing agents for graphite. The method of Hummer has some features compared to that of Brodie and Staudenmaier. Firstly, KMnO4 is a strong oxidant that aids in hastening the reaction so that the synthesis can be finished in a few hours. Secondly, the chlorate is not available, removing the probability of a ClO2 eruption. Thirdly, the exchange of fumigation with NaNO3 eliminates the acid haze generated by HNO315. To the best of our knowledge, there have been no studies comparing the effects of NiAl2O4, CuAl2O4, and ZnAl2O4 spinel aluminates, which were produced by the same synthetic method, on the performance of QDSSCs. Solar cells sensitized by quantum dots (QDSSCs) have attracted massive awareness in recent years, owing to their easy-fabrication procedure, low-cost, adjustable bandgap, and high theoretically mentioned power conversion efficiency (PCE) of up to 44%42. The photoelectrochemical technicality of QDSSCs has the same behavior as dye-sensitized solar cells (DSSCs), in which the solar cell is sensitized by the QDs instead of the dye molecules as a light absorber layer in QDSSCs43. A QDSSC is typically composed of a quantum dot sensitised photoanode film, an electrolyte containing a redox couple (i.e., S2/Sx2), and a counter electrode (CE) (i.e., Pt, and Cu2S)42,43,44. In spite of these qualities, however, the performance of the photovoltaic cells of most QDSSCs is much lower than that acquired from DSSCs. To date, much of the research work has concentrated on enhancing all the elements in QDSSCs. Since one of the essential reasons for low efficiency is the counter electrode interfaces, particular research efforts have settled on the expansion of congruous CEs for achieving simultaneous high efficiency and stable cells.

In the published literature, graphene-TiO2 nanocomposite has a large absorption band of visible light. The graphene-TiO2 nanocomposite photoanode has been deposited onto FTO using the doctor blade method as a photoanode to obtain a negative capacitance. Photovoltaic cells (PV) currently have a low efficiency in converting light into electrical power. Despite the superposition of several PV cells that convert more than 41% of incident light power to electricity and several semiconductor materials having an efficiency lower than 21% as a result of the great use of energy in the industry, these PVs can only convert one third of the light power received. This efficiency is limited by some physical properties of the materials, such as the Joule losses. The challenge of the scientific community is to prevent the leakage of electrons to energy. Most of the PV cells are prepared from semiconductor materials because of their very special properties. It can absorb photons of a well-defined wavelength to generate free electrons, which then gives an electric current. Several studies have shown that the GO can generate many pairs of electron-holes by absorbing one photon and relaxing the primary pair of electron-holes excited by illumination. Instead of losing excess excitation energy by the joule effect or phonon form, graphene is a suitable material to create hot charge carriers by transferring the excess energy to other carriers. The power conversion efficiency (η) and the short current Isc increased with the graphene amount due to the intrinsic properties of this material. The efficiency of the process is correlated to the energy lost by the joule effect or phonon form. The efficiency can be increased if the excited charge carriers use their excess energy to produce electron–hole pairs through an interaction carrier-carrier or a diffusion process, instead of losing energy in the form of heat and phonons. In particular, the best performing solar cells employing rGO exhibited power conversion efficiency (PCE) of up to 18.13%, while the control device without rGO delivered a maximum efficiency of 17.26%. An effective and low-cost approach has been proposed for the fabrication of reduced graphene oxide (rGO) solar cells. The hybrid composite of rGO has been synthesized by using a low-cost chemical method and deposited on a glass substrate by a doctor-blading process for application in heterojunction solar cells. The morphology, crystal phase, surface functional groups, and optoelectronic properties of the heterostructure have been explored. The J-V characteristics of the fabricated heterojunction cell show a power conversion efficiency of 4.35% (Voc = 0.51 V, Jsc = 14.47 mA cm−2, and fill factor (FF) = 51.60) due to the enhanced conductivity and charge transfer efficiency of the hybrid semiconductor. This simple approach assures the low-cost mass production of heterojunction solar cells45,46,47,48,49. Kafle et al. reported that the best performing solar cells employing rGO exhibited power conversion efficiency (PCE) of up to 18.13% in a perovskite cell composed of rGO as a counter electrode, while the control device without rGO delivered a maximum efficiency of 17.26%46. Kadhim et al., used the cell composed of TiO2 as a photoanode, CdS QDs, polysulphide electrolyte, and rGO as a counter electrode to give a PCE of 4.35%47. Mnasri et al., used the quantum dot sensitized solar cell composed of GO-TiO2 nanocomposites as a photoanode, five cycles of CdS QDs, polysulphide electrolyte and Pt as a counter electrode to give a PCE of 0.3%48.

In this work, for the first time, we have grown first-step, electrocatalytically active, highly stable CoAl2O4, NiAl2O4, CuAl2O4, and ZnAl2O4 spinel nanostructures by a sol–gel auto combustion technique as the working electrode in hybrid structures of ZnS/CdS quantum dots-based solar cells. The morphology of the surface and optical behavior of the aluminate spinels (MAl2O4 (M=Ni, Cu, Zn)) have been inspected by XRD, FT-IR, SEM, and UV–visible spectroscopy (UV–Vis). The effect of hybrid CdS QDSSC/ZnS QDs was also studied. The QDSSCs, which contain ZnAl2O4 as a photoanode, six cycles of CdS QDs as a photosensitized material, polysulphide electrolyte, and rGO as a counter electrode, gave a PCE of 8.22%. The cell contains a NiAl2O4 as a photoanode, twelve cycles of ZnS and CdS QDs, polysulphide electrolyte, and rGO as a counter electrode, given a PCE of 15.14%.

Materials Aluminum Nitrate (Al2(NO3)3.9H2O (97%, Aldrich), Zinc Acetate Zn(CH3COO)2 (97%, Bio Chem), Sodium Sulfide Na2S (98%, Alpha chemical), Ethanol absolute (99%, Bio Chem), Nitric acid HNO3 (Adwic), sulfuric acid H2SO4, (Dongwoo fin chem., 95–97%), Triton-X100 (97%, Aldrich), Extra pure graphite powder (12.0 g/ mole, 99.5%, Aldrich), Sulfur Powder (Adwic), Potasium Chloride (Advent), FTO (Fluorine-dopped SnO2) conductive glass (Aldrich), Nickle Chloride (NiCl2.6H2O), Cobalt Nitrate (Co(NO3)2) and Cupper Chloride (CuCl2.2H2O) from Adwic, Potassium Permanganate (KMnO4, Sigma Aldrich 97%), Hydrogen Peroxide (H2O2, Dongwoo fin chem., 30%).

The auto-combustion sol–gel method used for the synthesis of Al2O3 nanostructured, Al2 (NO3)3.9H2O was used as the precursor. Solution A contains a desired amount of aluminum nitrate nonahydrate and was dissolved in ethanol to prepare a 0.1 M of Al2 (NO3)2 ethanoic solution by stirring for about 2 h using a magnetic stirrer. Solution B contains a 30% ammonia solution. The gel of aluminum oxide was formed by adding the 30% ammonia solution dropwise to the aqueous aluminum nitrate solution under vigorous stirring for one h. This gel was left for 30 h at room temperature for maturation time and dried at 200 °C for 24 h. The resulting gel was annealed in a furnace for 4 h at 1100ºC11.

The M-Al2O4 spinel nanostructures were prepared by the sol–gel auto combustion method. Stoichiometric amounts of Al2 (NO3)3.9H2O and metal nitrate were dissolved in absolute ethanol to obtain a 0.2 M solution. Then, a convenient amount of DEA was added as fuel to the solution. The mixture was heated to 200 °C under continuous stirring until all of the ethanol had evaporated and the process took place. The mixed solution mutated into a condensed gel, which self-ignited to produce a pearly yellow powder for ZnAl2O416,26,50,51,52, a dark powder for CoAl2O4, a brown powder for CuAl2O421,24,25,30 and a grey powder for NiAl2O419,20,22,23. Finally, the as-synthesized powders were annealed in the air at 1100 °C for 4 h16.

Partially-reduced graphene oxide (P-rGO) was synthesized from the graphite powder according to the modified Hummers and Offman method37,38,39. In a solution containing 50 ml of concentrated H2SO4 and 50 ml of concentrated HNO3, the extra pure graphite powder (2.0 g) was pre-oxidized by slowly adding it to the mixture and stirring at 80 °C for 4 h. The mixture was cooled down to room temperature and then washed by de-ionized water until the pH value was neutral (equal to 7.0), followed by drying at 40 °C overnight. The resultant pre-oxidized graphite was dispersed into concentrated H2SO4 in a cold reaction vessel, which was kept in an ice bath and stirred. 10 g of KMnO4 was slowly added to it. During the addition, the temperature was kept below 10 °C. The mixture was stirred at 35 °C for 2 h until the solution became gelled and turned a brownish gray in color. Then 250 ml of de-ionized water was added and the temperature was put forward to 100 °C for 15 min, followed by adding 700 ml of de-ionized water and 30 ml of H2O2 to the mixture, stirred for 1 h. The solid products were composed from the solution after 12 h and washed with 5% HCl until sulphate ions were no longer detectable with BaCl2. Then the solid products were re-dispersed in de-ionized water five times to eliminate any impurities. Finally, the resultant sediment was dried at 60 °C for 4 h in an oven to yield the partially reduced graphene oxide P-r (GO)15,35,36,37,38,39. Fig. S1 shows the steps of rGO preparation step by step.

Both Al2O3 nanoparticle and M-Al2O4 nanocomposite films with a thickness of 0.052 mm were prepared and used for solar cell testing. The samples of Al2O3NP and M-Al2O4 nanocomposites were deposited onto conductive Fluorine-tin-oxide (FTO) glass substrates by the doctor-blading method using a dispersion of 0.2 g of Al2O3 powder in ethanol solution and the same of 0.2 g of CoAl2O4, CuAl2O4, NiAl2O4 and ZnAl2O4. Before spreading the film, the surfaces of the FTO substrates were cleaned for 30–60 min using an ultrasonicator. The substrates were then dried in air. The FTO boundaries of each substrate were covered with scotch tape to control the area of the film. The powder was first strewn in Triton-X100 and ethanol, and then the pending powder was added as drops in the midst of the substrate and prevalence to form a thick film to produce the film. The film was dried in the air for 30 min and then calcined at 300 °C for 5 min46,47,48,49,50,51,52,53.

The photo electrode was sensitized with the CdS QDs, which act as light absorbers by the Successive Ionic Layer Adsorption and Reaction (SILAR) method. To grow CdS QDs, the semiconductor film was immersed in a 0.2 M Cadmium nitrate (CdNO3)2 aqueous solution for 2 min as a Cd+2 source, then rinsed in ethanol to remove surplus ions and dried on a hot plate at 60 °C for 1 min. Then, the film was dipped into a 0.2 M Na2S aqueous solution for another 2 min to allow S2 to react with the pre-adsorbed Cd2+ leading to the formation of CdS QDs. Swiping the film in methanol and drying at 60 °C for 1 min removed the loosely bound S2−ions. On the other hand, the hybrid structures of ZnS/CdS QDs are prepared by the same method (SILAR) by the growth of ZnS QDs. The semiconductor film was immersed in a 0.2 M Zn (CH3COO)2 aqueous solution for 2 min before being rinsed with ethanol to remove the excess ions and dried for 1 min on a hot plate at 60 °C. Then, the film was dipped into a 0.2 M Na2S aqueous solution for another 2 min to allow S2 to react with the pre-adsorbed Zn2+, leading to the formation of ZnS QDs. The loosely bound S2−ions were removed by swiping the film in methanol and drying it at 60 °C for 1 min. Second, a semiconductor and ZnS QDs film were dipped into a 2 M Cd (NO3)2 aqueous solution as a Cd+2 source. Then, the film was dipped into a 0.2 M Na2S aqueous solution for another 2 min to allow S2−to react with the pre-adsorbed Cd2+, leading to the formation of hybrid structures of CdS QDs and ZnS QDs. The loosely bound S2−ions were removed by rinsing the film in methanol and then the film was dried at 60 °C for 1 min. To increase the crystallinity of QDs, the films with different quantum dot depositions were calcined at 300 °C for 5 min45.

A polysulfide electrolyte was prepared and used. The electrolyte is composed of 2 M Na2S, 2 M sulphur powder, and 0.2 M KCl mixed solution of methanol and deionized water with a volume ratio of 7:3 respectively. Electrolytes were deposited between the top of the QDs-coated anode and the counter electrode46.

The two electrodes, photo and counter electrodes, were clipped together facing each other using two clips, and the drops of electrolyte solution could then be put at the edges of the plates. The two warp clips are off and on, opening and closing while in place. An electrolyte is attracted to the space between the electrodes by capillary action. The light source was directed to each solar cell device, allowing light to penetrate the solar cell to the CdS QDs and CdS/ZnS adsorbed onto the Al2O3 NP and M-Al2O4 spinel film electrodes shown in Fig. S2.

The performance of the solar cell was measured using strained solar illumination with a 10.4 mW/cm2 light output. The short-circuit current and open-circuit voltage are measured by using photocell software, as well as calculating the cell efficiency. The light intensity source was measured by a radiometer (international light 1700). All the J-V curves of the solar cells were obtained in the dark and under illumination. The J-V characteristics as a function of incident light intensity were used to obtain the open-circuit voltage (Voc), short-circuit current density (Jsc), the maximum voltage point (Vmax), and the maximum current density point (Jmax).

Different techniques were used to examine the surface of prepared materials.

The X-ray diffraction patterns were reported using a Pan Analytical Model X 'Pert Pro, which was fitted with CuKα radiation (α = 0.1542 nm), a Ni-filter, and a general area detector. A 40 kV accelerating voltage and a 40 mA emission current were utilized. The diffractograms were measured in the 2θ range from 0.5 to 70 °.

The Fourier transform infrared spectroscopy (FT-IR) of the prepared samples was measured using the KBr technique adopted by the Nicolet Is-10 FT-IR spectrophotometer (Thermo Fisher Scientific). The KBr technique was conducted roughly in a quantitative manner for all samples, since the sample weight and that of KBr were both held constant.

A Field Emission Scanning Electron Microscope (FE-SEM) is used to examine the material's composition, particle size, and shape. For the samples prepared, a 30 kV acceleration voltage operating on a JSM-7500F electron microscope was reported.

Optical absorption spectra of the sample were analyzed using Ultraviolet–Visible absorption spectroscopy (Spectro UV–Vis 2800, United States).

Dielectric studies of Al2O3 NPs and M-Al2O4 NCs were executed as thin films on conducting glass (FTO) of dimension (6.25 cm2 surface area and a 0.052 mm thickness) for every sample to serve as electrodes during the measurements by a standard two-probe technique using an impedance analyzer (IM3570, Japan).

The X-ray diffraction pattern (XRD) for Al2O3 NPs, ZnAl2O4, NiAl2O4, CoAl2O4, and CuAl2O4 spinel is shown in Fig. 1. The XRD of highly crystalline α-Al2O3 shows the characteristic peaks at 35.17°, 43.379°, 45.47°, 52.55°, 57.516°, 66.513°, 68.218°, 73.42°, 75.16° and 83.778° corresponding to the crystal planes, (104), (311), (400), (006), (113), (024), (116), (211), (018) and (214), which confirmed the formation of Al2O3 NPs in a pure single hexagonal phase according to JCPDS Card No. 42-1468. Figure 3 shows the cubic spinel structure of NiAl2O4, which exhibited diffraction peaks at 25.73°, 38.006°, 43.87°, 49.593°, 51.626°, 66.306°, 67.59°, 72.146°, 81.966° and 86.046° corresponding to the crystal planes, (200), (220), (311), (400), (410), (422), (511), (440), (531) and (620), which confirmed the formation of a pure single phase of NiAl2O4, in agreement with JCPDS No. 10-033940,41,54,55. The strong and sharp diffraction peaks indicate that NiAl2O4 has a long-range ordered structure. Figure 1 shows a single phase of CuAl2O4 cubic spinel (JCPDS No. 33-0448) calcined at 1100 °C21,24,25,35,40. The Figure also depicts the characteristic CuAl2O4 peaks at 23.66°, 25.406°, 31.305°, 35.103°, 37.73°, 43.43°, 48.65°, 52.50°, 57.62°, 66.46°, 68.138°, 73.29 and 76.83° corresponding to the crystal planes, (511), (110), (111), (220), (311), (422), (311), (400), (422), (511), (440), (620) and (533). The formed peaks are congruent to the formation of ZnAl2O4 (JCPDS No. 05-0669)41,54,55 in a single phase structure with characteristic peaks at 35.599°, 38.28°, 40.079°, 51.37°, 60.36°, 66.76°, 69.12°, 71.78°, 72.86° and 80.89° corresponding to the crystal planes, (220), (311), (222), (400), (331), (422), (511), (440), (620) and (533). CoAl2O4, the characteristic peaks appear at 19.034°, 25.46°, 31.28°, 36.85°, 44.84°, 55.67°, 59.31°, 65.71°, 74.15°and 77.33° corresponding to the crystal planes, (220), (311), (222), (400), (331), (422), (511), (440), (620) and (533) (JCPDS No. 44-0160). In addition, the average crystallite size (D) of spinel aluminate nanostructures can be predestined from the full width at half maximum of the strongest diffraction peak by applying the Debye–Scherrer equation, Eq. (1). Table S1 shows the crystallite size, thickness of samples, and band gap energy.

XRD spectra of Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites at 1100 °C.

Figure 2 shows the typical transmittance FT-IR spectra of Al2O3 NPs, ZnAl2O4, NiAl2O4, CoAl2O4, and CuAl2O4 spinel oxides calcined at 1100 ℃ as a set of transmission peaks in the range of 400–4000 cm−1. The functional groups of aluminum oxide NPs and metal aluminate spinel structures were inspected by FT-IR analysis. The stretching mode of Al–O and the Al–O–Al bending mode in the spectrum of Al2O3 NPs appear at the peaks of 594 and 1598 cm−1, respectively. A band at 3451 cm−1 representing the –OH species was detected for the Al–OH bond formation. A small peak at 1634 cm−1 was attributed to the H–O–H bending vibration characteristic peak. This confirms the existence of water molecules absorbed on the surface of the Al2O3 NPs. Further, a sturdy absorption band at 1398 cm−1 occurs due to the distortion caused by the C–CH3, C–C, and C=O bonds. All the samples implicate concerted absorption bands around 3462, 2922, 2850, 2337, 1633, 1385, 1200, and 1118 cm−1 as shown in Fig. 2. Broad bands near 3462 and 1633 cm−1 are comforted to absorb water molecules' OH-stretching and bending vibrational modes, respectively27. Different IR studies of Al2O3 NPs and spinel metal aluminate nanocomposites observed the water absorption peaks and declared that the high surface area of these materials could result in swift adsorption of water from the atmosphere during pellet squeeze and IR mensuration27,56. C–H stretching vibration is represented by small peaks at around 2922 and 2850 cm−11. The absorption band at 2337 cm−1 is supposedly connected to the entity of CO2 on the surface powder, while a small peak at 1385 cm−1 can be attributed to the grout nitrogen groups output from the combustion reaction56. The peaks in the 1200 cm−1 region can be explained as vibrations of the C–C bond, and bands at around 1118 cm−1 can be related foremost to oxygen groups with a single C–O bond28,57. In the FT-IR spectrum of NiAl2O4 nanocomposites calcined at 1100 °C, the characteristic bands of NiAl2O4 appear around 3390, 1629, 725, and 478 cm−1, which would affirm the consistence of the NiAl2O4 aluminate spinel structure in good agreement with the XRD results29,58. These bands can be conformed to the uniform stretching, bending, and asymmetric stretching modes of Ni–O, Al–O, and Ni–O–Al bonds at octahedral and tetrahedral sites in M-Al2O4 spinel58. The FT-IR spectrum of CuAl2O4 nanocomposites calcined at 1100 ℃ confirms the formation of CuAl2O4 nanocomposites through the strongest four characteristic bands of CuAl2O4, which are 453, 501, 591, and 640 cm−124,25,58. The FT-IR spectrum of ZnAl2O4 nanocomposites calcined at 1100 °C shows sharp bands between 1634 and 3435 cm−1 (C–O and C–C vibration) and 1161 cm−1 (NO3− vibration), including the three OH vibration bands mentioned above. The bands lying at 1111, 668, and 490 cm−1 are comforted by the vibrations of Zn–O, Al–O, and Zn–O–Al bonds in ZnO4 tetrahedral and AlO6 octahedral groups in the spinel structure26,52,58. The spectrum of CoAl2O4 nanocomposites calcined at 1100 °C is also shown by FT-IR, with sharp bands between 2893 and 3335 cm−1 (C–O and C–C vibration) and at 1523 cm−1 (NO3− vibration). The bands lying at 1113, 670, and 565 cm−1 are confined to the vibrations of Co–O, Al–O, and Co–O–Al bonds, which confirmed the formation of CoAl2O4 nanocomposites.

FTIR spectra of Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites at 1100 °C.

Figure 3 Shows the FE-SEM images and elemental mapping allocation for the Al2O3 NPs, ZnAl2O4, CuAl2O4, NiAl2O4 and CoAl2O4 nanocomposites calcined at 1100 °C. FE-SEM images of the samples show uniform, spherical, and homogeneous nanoparticles of Al and Zn/Al with mean particle sizes of 29.77 and 44.66 nm, respectively. Figure 3(c) shows the smooth surface and the aggregation of the particles of Cu/Al with a particle size of 33.40 nm. As shown in Fig. 3(d,e), small spherical nanoparticles were neatly packed together with an identical size distribution, and the mean average particle size of NiAl2O4 and CoAl2O4 nanocomposites is in the ranges of 18.98–50.07 nm and 40.08–74.53 nm, respectively. In addition, the release of fragile gases such as CO2, N2, O2, and H2O during the combustion process should be one of the prime factors that create different pore structures in the ZnAl2O4, CuAl2O4, NiAl2O4, and CoAl2O4 nanocomposites. This interconnected pore structure is remarkable for catalytic applications. The amount of distribution is dependent on the homogeneity of the size of the particles. The EDX spectrum of Al2O3 NPs, ZnAl2O4, CuAl2O4, NiAl2O4, and CoAl2O4 obtained from FE-SEM is shown in Fig. 4(a–e), and the inset table shows the elemental analysis and wt. % of each element. EDX spectra analysis of the atomic% of the elements in ZnAl2O4, CuAl2O4, CoAl2O4, and NiAl2O4 nanocomposites was found to be 24.12/13.82 = 1.75, 25.17/13.28 = 1.89, 24.66/13.71 = 1.79, 8.31/3.98 = 2.09, respectively, for the best determination with the K-line series. This is in agreement with the results obtained from XRD. Fig. S3 depicts the photography and color of prepared samples as spinel aluminates after 1100 °C annealing.

FE-SEM of Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites at 1100 °C.

EDX analysis of (a)-Al2O3 NPs, (b)-CuAl2O4, (c)-CoAl2O4, (d)-ZnAl2O4 and (e)-NiAl2O4 nanocomposites.

The absorbance of pure Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites under UV–Vis irradiation decreases as the wavelength increases. In Fig. 5a, the optical absorbance of the pure Al2O3 NPs is 1.59% higher than the optical absorbance of ZnAl2O4, CoAl2O4, NiAl2O4 , and CuAl2O4 nanocomposites, which are (1.4%, 0.7%, 1.06%, and 0.6%), respectively, because the adding of metals like Zn, Co, Ni, and Cu has a high effect on the absorbance and causes a lower shift. Figure 5b shows the absorption spectra of ZnS QDs deposited on these samples to be ZnS/Al2O3, ZnS/ZnAl2O4, ZnS/CoAl2O4, ZnS/NiAl2O4 and ZnS/CuAl2O4. The ZnS/CoAl2O4 sample has a higher absorbance (2.78%) than ZnS/NiAl2O4, ZnS/CuAl2O4, ZnS/ZnAl2O4, and ZnS/Al2O3, which are (2.65%, 2.52%, 2.39%, and 2.21%) because ZnS QDs are more sensitive to light and rapidly make a shift in absorption edge. Figure 5c shows the absorption spectra of CdS QDs deposited on these samples to be CdS/Al2O3, CdS/ZnAl2O4, CdS/CoAl2O4, CdS/NiAl2O4, and CdS/CuAl2O4, where the CdS/CuAl2O4 sample has a higher absorbance (2.9%) than CdS/Al2O3, CdS/ZnAl2O4, CdS/CoAl2O4, and CdS/NiAl2O4, which are (2.74%, 2.83%, 2.54%, and 2.63%, respectively). Figure 5d shows the absorption spectra of the hybrid structures of (CdS/ZnS) QDs deposited on these samples to be CdS/ZnS/Al2O3, CdS/ZnS/ZnAl2O4, CdS/ZnS/CoAl2O4, CdS/ZnS/NiAl2O4, and CdS/ZnS/CuAl2O4, where the CdS/ZnS/CuAl2O4 sample has a higher absorbance (2.93%) than CdS/ZnS/Al2O3, CdS/ZnS/ZnAl2O4, CdS/ZnS/NiAl2O4 and CdS/ZnS/CoAl2O4, which are (2.88%, 2.82%,2.75% and 2.5%, respectively). In addition, comparison between the prepared materials and the same method was done by using the same thickness of these materials.

Absorbance spectra of (a)-Pure MAl2O4, (b)-ZnS/MAl2O4, (c)-CdS/MAl2O4 and (d)-CdS@ZnS/MAl2O4.

To know the optical bandgap, we have made an itemized calculation of the band gap using the Tauc formula; (αhν) = A (hυ − Eg) n, where, α is the absorption coefficient, hυ is the photon energy, Eg is the energy gap, and n is the quality of the transitions. The term n is taken as ½ for direct transition and 2 for indirect transition. The optical bandgap energy is investigated by plotting (αhυ) 1/n versus photon energy and drawing the tangent to the curve that intersects with the energy axis at α = 0. The Tauc plot of pure Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites for direct allowed transition is shown in Fig. S4a. The estimated energy gaps of Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4 and CuAl2O4 nanocomposites are 1.37 eV, 1.5 eV, 1.83 eV, 1.59 eV and 2.07 eV, respectively. The Tauc plots of ZnS/Al2O3 and ZnS/MAl2O4 in direct allowed transition are shown in Fig. S4b, and the estimated energy band gaps of ZnS/Al2O3, ZnS/ZnAl2O4, ZnS/CoAl2O4, ZnS/NiAl2O4, and ZnS/CuAl2O4 are 1.61 eV, 1.67 eV, and 1.13. The Tauc plots of CdS/Al2O3 and CdS/MAl2O4 in direct allowed transition are shown in Fig. S4c, and the estimated energy band gaps of CdS/Al2O3, CdS/ZnAl2O4, CdS/CoAl2O4, CdS/NiAl2O4, and CdS/CuAl2O4 are 1.58 eV, 1.38 eV, and 1.33. The Tauc plots of CdS/ZnS/Al2O3 and CdS/ZnS/MAl2O4 in direct allowed transition are shown in Fig. S4d, as are the estimated energy band gaps of CdS/ZnS/Al2O3, CdS/ZnS/ZnAl2O4, CdS/ZnS/CoAl2O4, CdS/ZnS/NiAl2O4, CdS/ZnS/CuAl2O4 are 1.57 eV, 1.42 eV, 1.64 eV, 1.66 eV, and 1.38 eV, respectively. The absorption coefficient of different materials is calculated by this equation, where (A) is the absorbance of material and (t) is the thickness of it. The thickness of thin films is constant for all materials. The presence of metals like Co, Ni, Zn, and Cu has an effect on the energy gap of materials by decreasing it and contributing to narrowing the band gap of the main semiconductor. All the energy gaps for all materials are listed in the below Table S2.

The impedance of Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites with CdS QDs on FTO conductive glass through the dark field was determined by electrochemical impedance spectroscopy (EIS) and can be illustrated by the kinetic operation of charge relocated in QDSSCs. Figure 6 shows one semicircle and the second semicircle appears as a straight diffusion line due to the presence of CdS quantum dots in the Nyquist plot of each sample and the same behavior of the samples with CdS@ZnS QDs. The data for samples gives the values of charge transport resistance, Rct for the first semicircle arc and charge recombination resistance (Rrec) for the second semicircle arc at high frequency and low frequency, respectively. The good adhesion of the bond between ZnAl2O4 nanostructures and the FTO conductive glass substrate pointed to the lower Rct value, which supports more electrons from the external circuit. Charge transfer resistance is of primary significance because it eases the carry of electrons during the catalytic reduction process of an electrolyte. A high electron mobility rate is achieved by a lower value of Rct and causes high electrical outputs, and vice versa. Table 1 shows the relaxation times, diffusion rates, and the Rct value of the ZnAl2O4 electrode (7.31 Ω.cm2) is lower than that of the CuAl2O4 electrode (7.56 Ω.cm2), the NiAl2O4 electrode (10.94.cm2), the Al2O3 electrode (7.81 Ω.cm2), and the CoAl2O4 electrode (10.5 Ω.cm2) with CdS QDs59,60. Due to the good electrocatalytic attitude of ZnAl2O4, it can behave as an efficient WEs catalyst to minimize the oxidized polysulphide electrolyte and high electron mobility rate desired for good photovoltaic performance of QDSSCs. Fig. S6 shows the equivalent circuit of QD deposition on nanomaterial preparation.

Nyquist plot of EIS spectra of CdS QDs deposited on Al2O3 NPs and MAl2O4 (M=Cu, Co, Ni, and Zn) nanocomposites as WEs on FTO.

The good adhesion bonding of the nanostructures and the FTO conductive glass substrate enables them to achieve a lower Rct value than NiAl2O4, which elevates more electrons from the external circuit. The relocating of electrons during the catalytic reduction process of an electrolyte is facilitated by charge transfer resistance. A lower value of Rct leads to a high electron mobility rate and causes high electrical outputs, and vice versa. Table 2 shows the relaxation times, diffusion rates, and the Rct value of the NiAl2O4 electrode (8.11 Ω cm2) is lower than that of the CuAl2O4 electrode (8.31 Ω.cm2), the Al2O3 electrode (44.75 Ω.cm2), the ZnAl2O4 electrode (49.56 Ω.cm2), and the CoAl2O4 electrode (8.63 Ω.cm2) with hybrid structures of CdS@ZnS QDs59,60. Due to the good electrocatalytic attitude of the CuAl2O4, it can be behave as an efficient WEs catalyst to minimize the oxidized polysulphide electrolyte and high electron mobility rate desired for good photovoltaic performance of QDSSCs. The kinetic operation of charge transport in QDSSCs, electrochemical impedance spectroscopy (EIS), was executed through the exposition of Al2O3 NPs, ZnAl2O4, CoAl2O4, NiAl2O4, and CuAl2O4 nanocomposites on FTO conductive glass, where by increasing relaxation time, the diffusion rate is decreased, consequently increasing the power activity of the photoanode in the solar cell, which includes the increasing migration of quantum dots on the semiconductor surface in addition to increasing the motion of free electrons in the cell, as indicated by the obtained data. The equivalent circuit is represented in Fig. S6. From the following equation, the diffusion rate of electrons can be calculated from Eq. (3), the lifetimes (relaxation times) of photogenerated electrons (τn) Eq. (4):

Figs. S5a,b show the J-V characteristics of the first systems of QDSSCs composed of Al2O3 NPs, ZnAl2O4, NiAl2O4, CoAl2O4, and CuAl2O4 nanocomposites as a photoanode with CdS QDs as a photosensitized nanomaterial and P-rGO as a counter electrode, and the second system composed of the same photoanode and counter electrode with hybrid structures of (CdS@ZnS) under one sun illumination (10.4 mW*cm−2), respectively. Tables 3 and 4 also summarize the photovoltaic parameters (Jsc, Voc, and η) and cell configuration. The power conversion efficiency of the first system consists of six layers of CdS QDs giving the higher efficiency of ZnAl2O4 nanocomposites (8.22%) surface based on P-rGO CE compared to the efficiency of Al2O3 NPs, NiAl2O4, CoAl2O4, and CuAl2O4 (5.77%, 1.84%, 4.15%, and 6.32%), respectively, shown in Table 3, because ZnAl2O4 has high chemical, mechanical stability, great separation and transfer of light-generated electrons and holes, which corresponds to the current density of 22.86 mA*cm−2 and fill factor 0.58. (ZnAl2O4) nanocomposite with CdS QDs has the highest efficiency. This is due to several reasons:

It has the smallest crystallite size as indicated by XRD (Table S1).

It has the lowest band-gap energy (Table S2).

It has the lowest charge transport resistance (Rct = 7.31*104), charge recombination resistance (Rrce = 11.5*105), diffusion rate (Keff = 9.09), and the highest lifetime of the photogenerated electrons (τn = 11*10−2) as indicated by the electrochemical performance (Table 1).

Zinc oxide has some advantages such that it is a common wide band-gap semiconductor that is now being investigated due to its wide range of applications and adjustable features. The ZnO nanoparticles' wide band-gap semiconductor characteristics are also beneficial in inducing intracellular reactive oxygen species (ROS) production. Conduction electrons (e) and valence holes (h +) in semiconductors have long been employed for photocatalytic oxidation of organic and inorganic contaminants. However, sufficient electrons and holes were routinely generated using UV irradiation and excitation. Even in normal light conditions, great quantities of holes and/or electrons may be accessible in ZnO nanoparticles. P. Sakthivel et al. (2022) show that in the zone wherein light absorption occurs owing to band gap excitation, which reveals that increasing the optical absorption of ZnO by adding defects (such as metal ion doping) to its surface can improve its optical absorption. Aluminum (Al) ions doped on the surface of ZnO nanoparticles boosted the generation of electrons and/or holes in a previous study49,50,51,52,53. The second system based on the twelve layers of hybrid structures of CdS@ZnS QDs on the NiAl2O4 nanocomposite film with P-rGO CE exhibited η of 15.14%. A noticeable improvement in efficiency was observed compared to the cell of Al2O3 NPs, ZnAl2O4, CoAl2O4 and CuAl2O4 (5.65%, 2.79%, 8.86%, and 12.55%), respectively, shown in Table 4. These photovoltaic improvements in the cells are based on the hybrid structures of CdS@ZnS layers on the NiAl2O4 photoanode with P-rGO CE. The conversion efficiency of the cell η can be determined by the equation below:

where JSC is the short circuit current density, VOC is the open circuit voltage, FF is the fill factor, and Pin is the power intensity of the incident light. From the J-V curves, FF values can be determined.

Aluminum Oxide nanoparticles and spinel metal aluminate nanocomposites have been successfully prepared by the auto-combustion sol–gel method. The electrochemical performance of metal aluminates Al2O3 NPs and MAl2O4 (M=Zn, Co, Ni, and Cu) is greatly affected by the loading of different quantum dots (CdS) and hybrid structures (CdS/ZnS). The hybrid structures of (CdS/ZnS) on metal aluminates showed a high rendering as photoanodes in QDSSCs, whereby by increasing the life time of quantum dots, the diffusion rate is decreased and the (PCE) increased. The highest activity was 15.14% in the cell containing NiAl2O4 spinel with (CdS/ZnS) QDs. The EIS analysis showed that NiAl2O4 has the lowest diffusion rate, Keff, and the highest electron life time, τn.

All data generated or analysed during this study are included in this published article (and its Supplementary Information files).

Singh, K., Barai, D. P., Chawhan, S. S., Bhanvase, B. A. & Saharan, V. K. Synthesis, characterization and heat transfer study of reduced graphene oxide-Al2O3 nanocomposite based nanofluids: Investigation on thermal conductivity and rheology. Mater. Today Commun. 26, 101986 (2021).

Mahmoud, S. A., Fouad, O. A., Salem, A. A. & Bendary, S. H. Profound impact of Zn3(OH)2(V2O7)(H2O)2 and Zn3V2O8–Zn2V2O7 in dye sensitized solar cells. J. Electron. Mater. 50, 4289–4302 (2021).

Article  ADS  CAS  Google Scholar 

Mahmoud, S. A., Mohamed, B. S. & Killa, H. M. Synthesis of different sizes TiO2 and photovoltaic performance in dye-sensitized solar cells. Front. Mater. 8, 714835 (2021).

Sujiono, E. H. et al. Graphene oxide based coconut shell waste: Synthesis by modified hummers method and characterization. Heliyon 6, 04568 (2020).

Su, S. Y. et al. Preparation of CuAl2O4 submicron tubes from electrospun Al2O3 fibers. Ceram. Int. 45, 1439–1442 (2019).

Mahmoud, S. A. et al. Specific capacitance of CoS encapsulated g-C3N4 core shell nanocomposite as extremely efficient counter electrode in quantum dots sensitized solar cells. J. Solid State Electrochem. 25, 2345–2360 (2021).

Guo, T. et al. “Stretched graphene nanosheets formed the ‘obstacle walls’ in melamine sponge towards effective electromagnetic interference shielding applications. Mater. Des. 182, 108029 (2019).

Luo, J., Wang, J., Xia, F. & Huang, X. Direct growth of large area uniform double layer graphene films on MgO(100) substrates by chemical vapor deposition. Mater. Chem. Phys. 233, 213–219 (2019).

Wang, J. et al. Ultra-thin, highly graphitized carbon nanosheets into three dimensional interconnected framework utilizing a ball mill mixing of precursors. Chem. Eng. J. 374, 1214–1220 (2019).

Gupta, M., Singh, V. & Katyal, P. Synthesis and structural characterization of Al2O3 nanofluids. Mater. Today: Proc. 5, 27989–27997 (2018).

Cinar, A., Baskut, S., Seyhan, A. T. & Turan, S. Tailoring the properties of spark plasma sintered SiAlON containing graphene nanoplatelets by using different exfoliation and size reduction techniques: Anisotropic mechanical and thermal properties. J. Eur. Ceram. Soc. 38(4), 1299–1310 (2018).

Hessein, A. & El-Moneim, A. A. Synthesis of copper sulfide/reduced graphene oxide nanocomposites for use as the counter electrodes of high-performance CdS-sensitized solar cells. New Carbon Mater. 33(1), 26–35 (2018).

Gilabert, J. et al.Fuel effect on solution combustion synthesis of Co(Cr, Al)2O4 pigments.Bulletin of the Spanish Society of Ceramics and Glass.56, 215–225 (2017).

Alam, S. N., Sharma, N. & Kumar, L. Synthesis of graphene oxide (GO) by modified hummers method and its thermal reduction to obtain reduced graphene oxide (rGO). Graphene 6(1), 1–18 (2017).

Liu, Q., Gong, Y., Wang, T., Chan, W. L. & Wu, J. Metal-catalyst-free and controllable growth of high-quality monolayer and AB-stacked bilayer graphene on silicon dioxide. Carbon 96, 203–211 (2016).

Tangcharoen, T., T-Thienprasert, J. & Kongmark, C. Optical properties and versatile photocatalytic degradation ability of MAl2O4 (M=Ni, Cu, Zn) aluminate spinel nanoparticles. J. Mater. Sci.: Mater. Electron. 29, 8995–9006 (2018).

Aguilar, C. G. et al. Effect of calcination temperature on structure and thermoelectric properties of CuAlO2 powders. J. Mater. Sci. 53, 1646–1657 (2018).

Han, M. et al. Physical properties of MgAl2O4, CoAl2O4, NiAl2O4, CuAl2O4, and ZnAl2O4 spinels synthesized by a solution combustion method. Mater. Chem. Phys. 215, 251–258 (2018).

He, Y. & Shih, K. Nano-indentation on nickel aluminate spinel and the influence of acid and alkaline attacks on the spinel surface. Ceram. Int. 38, 3121–3128 (2012).

Ragupathi, C. et al. Comparative investigation of nickel aluminate (NiAl2O4) nano and microstructures for the structural, optical and catalytic properties. Polyhedron 72, 1–7 (2014).

Kumar, R. T. et al. Comparative study of nano copper aluminate spinel prepared by sol–gel and modified sol–gel techniques: Structural, electrical, optical and catalytic studies. J. Alloys Compd. 522, 39–45 (2012).

Koonsaeng, N., Laobuthee, A. & Hasin, P. Controllable synthesis of metallo-alkoxide precursor-derived nickel aluminate spinels using TEA-gel process and morphology-dependent reducibility. Mater. Chem. Phys. 182, 287–297 (2016).

Nazemi, M. K. et al. Preparation of nanostructured nickel aluminate spinel powder from spent NiO/Al2O3 catalyst by mechano-chemical synthesis. Adv. Powder Technol. 23, 833–838 (2012).

Hu, C. Y., Shih, K. & Leckie, J. O. Formation of copper aluminate spinel and cuprous aluminate delafossite to thermally stabilize simulated copper-laden sludge. J. Hazard. Mater. 181, 399–404 (2010).

Article  CAS  PubMed  Google Scholar 

Arjmand, M. et al. Evaluation of CuAl2O4 as an oxygen carrier in chemical-looping combustion. Ind. Eng. Chem. Res. 51, 13924–13934 (2012).

Ge, D. L. et al. Facile synthesis of highly thermostable mesoporous ZnAl2O4 with adjustable pore size. J. Mater. Chem. A 1, 1651–1658 (2013).

Wei, X. H. & Chen, D. H. Synthesis and characterization of nanosized zinc aluminate spinel by sol–gel technique. Mater. Lett. 60, 823–827 (2006).

Buvaneswari, G., Aswathy, V. & Rajakumari, R. Comparison of color and optical absorbance properties of divalent ion substituted Cu and Zn aluminate spinel oxides synthesized by combustion method towards pigment application. Dye Pigment 123, 413–419 (2015).

Staszak, W., Zawadzki, M. & Okal, J. Solvothermal synthesis and characterization of nanosized zinc aluminate spinel used in iso-butane combustion. J. Alloys Compd. 492, 500–507 (2010).

Salavati, N. M., Davar, F. & Farhadi, M. Synthesis and characterization of spinel-type CuAl2O4 nanocrystalline by modified sol–gel method. J. Sol-Gel Sci. Technol. 51, 48–52 (2009).

Mahmoud, S. A., Bendary, S. H. & Martin, H. A. Effect of different electrolytes on the efficiency of dye sensitized solar cells for solar energy conversion. J. Nanosci. Nanotechnol. 6, 3719–3728 (2017).

Mahmoud, S. A., Atia, H. & Bendary, S. H. Synthesis of a high efficiency novel working electrode scandium/HOMBIKAT in dye-sensitized solar cells. Sol. Energy 134, 452–460 (2016).

Article  ADS  CAS  Google Scholar 

Dolla, T. H. et al. Sol-gel synthesis of MnxNi1–xCo2O4 spinel phase materials: Structural, electronic, and magnetic properties. J Alloys Compd 742, 78–89 (2018).

Gupta, M., Singha, V. & Katyal, P. Synthesis and structural characterization of Al2O3 nanofluids. Mater. Today: Proc. 5, 27989–27997 (2018).

Jastrz˛ebska, A. M. et al. Synthesis of the RGO/Al2O3 core–shell nanocomposite flakes andcharacterization of their unique electrostatic properties using zetapotential measurements. Appl. Surf. Sci. 362, 577–594 (2016).

Guerrero-Contreras, J. & Caballero-Briones, F. Graphene oxide powders with different oxidation degree, prepared by synthesis variations of the hummers method. Mater. Chem. Phys. 153, 209–220 (2015).

Chen, J., Li, Y., Huang, L., Li, C. & Shi, G. High-yield preparation of graphene oxide from small graphite flakes via an improved Hummers method with a simple purification process. Carbon 81, 826–834 (2015).

Ramesha, G. K., Vijaya Kumara, A., Muralidhara, H. B. & Sampath, S. Graphene and graphene oxide as effective adsorbents toward anionic and cationic dyes. J. Colloid Interface Sci. 361(1), 270–277 (2011).

Article  ADS  CAS  PubMed  Google Scholar 

Song, J., Wang, X. & Chang, C. T. Preparation and characterization of graphene oxide. J. Nanomater. 2014, 1–6 (2014).

Zhang, C. et al. Graphene oxide reduced and modified by environmentally friendly glycylglycine and its excellent catalytic performance. Nanotechnology 25(13), 135707 (2014).

Article  ADS  PubMed  Google Scholar 

Zheng, Q., Li, Z., Yang, J. & Kim, J.-K. Graphene oxide-based transparent conductive films. Prog. Mater. Sci. 64, 200–247 (2014).

Hagfeldt, A., Boschloo, G., Sun, L. C., Kloo, L. & Pettersson, H. Dye-sensitized solar cells. Chem. Rev. 110, 6595–6663 (2010).

Article  CAS  PubMed  Google Scholar 

Hod, I. & Zaban, A. Materials and interfaces in quantum dot sensitized solar cells. Chall. Adv. Prospect. Langmuir 25, 7264–7273 (2014).

Fan, S. Q. et al. Ordered multimodal porous carbon as highly efficient counter electrodes in dye-sensitized and quantum-dot solar cells. Langmuir 26(16), 13644–13649 (2010).

Article  CAS  PubMed  Google Scholar 

Erdi, A. et al. Improving performance and stability in quantum dot-sensitized solar cell through single layer graphene/Cu2S nanocomposite counter electrode. Renew. Energy 145, 219–2200 (2020).

Bhim, P. K. Application of reduced graphene oxide (rGO) for stability of perovskite solar cells. Surf. Eng. Graphene 978, 30207 (2019).

Kadhim, A. K., Mohamed, R. & Atheer, I. Enhancing the efficiency of perovskite solar cells by modifying perovskite layer with rGO additive. Chem. Phys. Lett. 786, 139189 (2022).

Mnasria, G. et al. Characterization and study of CdS quantum dots solar cells based on graphene-TiO2 nanocomposite photoanode. Results Phys. 18, 103253 (2020).

Akhtar, M. J., Alhadlaq, H. A., Alshamsan, A., Majeed Khan, M. A. & Ahamed, M. Aluminum doping tunes band gap energy level as well as oxidative stress-mediated cytotoxicity of ZnO nanoparticles in MCF-7 cells. Sci. Rep. 1038, 13876 (2015).

de Macedo, H. P. et al. Characterization of ZnAl2O4 spinel obtained by hydrothermal and microwave assisted combustion method: Comparative. Mater. Res. 1590, 1980–5373 (2017).

Pathak, S. K., Verma, A. & Verma, A. Shifting optical-luminescence properties of ZnAl2O4:Eu, dye phosphor by urea fuel combustion synthesis. Condens. Matter. Appl. Phys. 978, 7354 (2020).

Sakthivel, P., Saravanakumar, K. & Sankaranarayanan, R. K. Influence of Sn4+ ion on band gap tailoring, optical, structural and dielectric behaviors of ZnO nanoparticles. Spectrochimica Act Part A: Mol. Biomol. Spectrosc. 267, 120487 (2022).

Sameera, S., Vidyadharan, V., Sasidhran, S. & Gopchandran, K. G. Nanostructured zinc aluminates: A promising material for cool roof coating. J. Sci. Adv. Mater. Dev. 4, 524–530 (2019).

Yu, H., Zhang, B., Bulin, C., Li, R. & Xing, R. High-efficient synthesis of graphene oxide based on improved hummers method. Sci. Rep. https://doi.org/10.1038/srep36143 (2016).

Article  PubMed  PubMed Central  Google Scholar 

Hummers, W. S. & Offeman, R. E. Preparation of graphitic oxide. J. Am. Chem. Soc. 80(6), 1339 (1958).

Pedram, M. Z., Omidkhah, M. & Amooghin, A. E. Synthesis and characterization of diethanolamine-impregnated cross-linked polyvinylalcohol/glutaraldehyde membranes for CO2/CH4 separation. J. Ind. Eng. Chem. 20, 74–82 (2014).

Samkaria, R. & Sharma, V. Effect of rare earth yttrium substitution on the structural, dielectric and electrical properties of nanosized nickel aluminate. Mater. Sci. Eng. B 178, 1410–1415 (2013).

Ye, M. et al. Quantum-dot sensitized solar cells employing hierarchical Cu2S microspheres wrapped by reduced graphene oxide nanosheets as effective counter electrodes. Adv. Energy Mater. 41, 301564–1301572 (2014).

Noam, A. Relaxation times in diffusion processes. J. Chem. Phys. 82, 935–938 (1985).

Smaihi, M., Petit, D., Boilot, J. P., Botter, F. M. & Mougin, J. Transport properties and tritium release of sol–gel lithium orthosilicate ceramics. In Fusion Technology 817–821 (Elsevier, 1990).

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Egyptian Petroleum Research Institute, Nasr City, Cairo, 11727, Egypt

Physics Department, Faculty of Science, Zagazig University, Zagazig, Egypt

Mostafa E. Elsisi & Asma F. Mansour

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

Dr. S.A.M.: Conceptualization, Methodology, Investigation, Writing-Reviewing & Editing. M.E.E.: Methodology, Data collection, analysis, Investigation, Writing-draft, review the manuscript. A.F.M.: Conceptualization, Methodology, Investigation, Writing-Reviewing & Editing.

Correspondence to Sawsan A. Mahmoud.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Mahmoud, S., Elsisi, M.E. & Mansour, A.F. Synthesis and electrochemical performance of α-Al2O3 and M-Al2O4 spinel nanocomposites in hybrid quantum dot-sensitized solar cells. Sci Rep 12, 17009 (2022). https://doi.org/10.1038/s41598-022-21186-4

DOI: https://doi.org/10.1038/s41598-022-21186-4

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Scientific Reports (Sci Rep) ISSN 2045-2322 (online)

Synthesis and electrochemical performance of α-Al2O3 and M-Al2O4 spinel nanocomposites in hybrid quantum dot-sensitized solar cells | Scientific Reports

CAS 1313-97-9 Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.